4A Molecular Sieve, 3-5mm, Used in Gas and Liquid Drying

We uphold the core values of 'creating value for customers, sharing value with employees, and dedicating value to society', and continue to devote ourselves to creating better Alumina Grinding Ball grinding media, activated alumina ball, Alumina Grinding Ball solutions. Your recognition and trust is a beacon to guide our long-term development and sustainable operation. We think that only by continuous self-improvement and enhancement of innovation ability can we maintain our brand and competitiveness.

Molecular sieves (also known as synthetic zeolites) are aluminosilicate microporous crystals, which are composed of SiO and AIO tetrahedra and have a framework structure.

Metal cations (such as Na, K, Ca, etc.) are present in the zoelite lattice to balance the excess negative charges in the tetrahedron.

The main component of type A is aluminosilicate, with a pore size of 4A (1A=10 -10 m), which is called 4A (also known as nano-A) kind; the Na+ in the 4A kind is exchanged with Ca2+ to form a pore size of 5A, which is 5A (also known as calcium type A) zoelite sieve; exchange Na+ of 4A zeolite with K+ to form the pore size of 3A, which is 3A (also known as potassium A type) zeolite sieve.

The crystal structure of X-type aluminosilicate is different (the ratio of silicon to aluminum is different), forming molecular sieve crystals with a pore size of 9-10A, which is called 13X (also known as sodium X-type) ; exchange Na+ in 13X with Ca2+, A molecular sieve crystal with a pore size of 9A is formed, which is called 10X (also known as calcium X type) zeolite sieve.

Product Range:

Character of Service

Strong ability of molecular sieve hygroscopic, used for gas purification processing, should be avoided when saving deposit directly exposed to the air for a long time and has hygroscopic and should be done before the molecular sieve using regeneration of molecular sieve avoid oil and liquid water use should avoid contact with oil and liquid water dry processing of the gas in the industrial production, air, hydrogen, oxygen, nitrogen, argon, etc. With two adsorption dryer in parallel, a job, at the same time, the other one can undertake work alternates regeneration process and regeneration, to ensure the equipment run continuously dryer work under 8 to 12, air flushing regeneration under heating to 350The regeneration temperature of molecular sieves with different specifications is slightly different. The molecular sieves have good catalytic effect on some organic gases.

Index

Item		Hydration Catalyst
Color		White
Aperture		ZSM-5 Molecular Sieve Calalyst
Shape		Powder
Size(mm)	2-3μm	2-3μm
Molar	26-40	26-40
Ratio(SiO2/Al2O3)	≥0.35	≥0.45
Acid(mmol/g)	≤5	≤2
Cl(ppm)	≤1000	≤300
Polymorph		Na1.78Al2Si31.1066.1
Operating Conditions
Reaction Temperature		100-130℃
Reaction Pressure		0.5-1.0Mpa(g)
Catalyst-Oil Ratio		0.46
WOR		3:1
Cycloethylene Conversion Rate		≥10%
Cycloethylene Selevtivity		≥98.5%
Application		Catalyst for Cyclohexene Hydration
		Producing the Cyclohecanol
		Zeolite Molecular Sieve

Our Lab

With the technology innovation and constant commitment to our customers, we are confident to be your first choice of professional 4A Molecular Sieve, 3-5mm, Used in Gas and Liquid Drying. We are able to supply top quality items, aggressive price and greatest buyer assistance. While relentlessly pursuing "innovative technology, excellent products, and high-end experience", our company is becoming an professional company that can help employees realize their dreams, and provide customers with value-for-money enjoyment.

Hot Tags: molecular sieve for liquid drying, China, manufacturers, suppliers, factory, wholesale, price, RSC 2006 Catalyst, Calcined Alumina Powder For Wear Resistant, Boehmite, Calcined Aluminum Oxide For Polishing, kraus sulfur catalysis, MTBE Etherification Strong Acid Catalyst